C63000 (Aluminum Bronze)
C63000 (Aluminum Bronze)
US EPA Registered Antimicrobial
Chemical Composition
(%max., unless shown as range or min.)
Cu(1) Al Fe MnNi(2) Si Sn Zn
Min./Max.Rem.9.0-11.02.0-4.01.54.0-5.5.25.20.30
Nominal 82.0 10.0 3.0 - 5.0 - - -
(1) Cu value includes Ag.
(2) Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.5% min.
Mechanical Properties (measured at room temperature, 68 F (20 C)
TemperSection
Size
Cold
Work
Typ/
Min Temp Tensile
Strength
Yield
Strength
(0.5% ext.
under load)
Yield
Strength
(0.2%
offset)
Yield
Strength
(0.05%
offset)
El Rockwell
Hardness
Vickens
Hard.
Brinell
Hard.
Shear
Strength
Fatigue
Strength*
Izod
Impact
Strength
in. % F ksi ksi ksi ksi % B CF30T 500 5003000ksi ksi ft-lb
mm. C MPa MPa MPa MPa MPa MPa J
Rod
M30 4 0 TYP68 100 60 - - 1596- - - - - - 62 36 0.0
102 20 689 414 - - 1596- - - - - - 427 248 0.0
Bar
HR50 2 10 TYP68 100 60 - - 1596- - - - - - - - 0.0
51 20 689 414 - - 1596- - - - - - - - 0.0
Rod
HR50 3 10 TYP68 112 62 - - 2096- - - - - - 65 37 0.0
76 20 772 427 - - 2096- - - - - - 448 255 0.0
Bar
M30 3 0 TYP68 90 50 - - 1596- - - - - - - - 0.0
76 20 621 345 - - 1596- - - - - - - - 0.0
Rod
HR50 1 10 TYP68 118 75 - - 1598- - - - - - 70 37 0.0
25.4 20 814 517 - - 1598- - - - - - 483 255 0.0
Bar
HR50 1 10 TYP68 110 62 - - 1597- - - - - - - - 0.0
25.4 20 758 427 - - 1597- - - - - - - - 0.0
Rod
HR50 2 10 TYP68 115 65 - - 1896- - - - - - 69 38 0.0
51 20 793 448 - - 1896- - - - - - 476 262 0.0
*Fatigue Strength: 100 x 10 6
cycles,
unless indicated as [N]X 106
.